Asset Details
Do you wish to reserve the book?
Fly-Ash-Based Geopolymers Reinforced by Melamine Fibers
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Fly-Ash-Based Geopolymers Reinforced by Melamine Fibers
Do you wish to request the book?
Fly-Ash-Based Geopolymers Reinforced by Melamine Fibers
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Fly-Ash-Based Geopolymers Reinforced by Melamine Fibers
2021
Overview
This paper presents the results of research on geopolymer composites based on fly ash with the addition of melamine fibers in amounts of 0.5%, 1% and 2% by weight and, for comparison, without the addition of fibers. The melamine fibers used in the tests retain their melamine resin properties by 100% and are characterized by excellent acoustic and thermal insulation as well as excellent filtration. In addition, these fibers are nonflammable, resistant to chemicals, resistant to UV radiation, characterized by high temperature resistance and, most importantly, do not show thermal-related shrinking, melting and dripping. This paper presents the results of density measurements, compressive and flexural strength as well as the results of the measurement of thermal radiation changes in samples subjected to a temperature of 600 °C. The results indicate that melamine fibers can be used as geopolymer reinforcement. The best result was achieved for 0.5% by weight amount of reinforcement, approximately 53 MPa, compared to 41 MPa for a pure matrix. In the case of flexural strength, the best results were obtained for the samples made of unreinforced geopolymer and samples with the addition of 0.5% by weight of melamine fibers, which were characterized by bending strength values above 9 MPa, amounting to 10.7 MPa and 9.3 MPa, respectively. The thermal radiation measurements and fire-jet test did not confirm the increasing thermal and fire resistance of the composites reinforced by melamine fiber.
Publisher
MDPI AG
Subject
/ Cement
/ Concrete
/ Fibers
/ Fly ash
/ Melamine
/ Melamine formaldehyde resins
/ Modulus of rupture in bending
/ Polymers
/ Sodium
/ Weight