Asset Details
Do you wish to reserve the book?
Structure and properties of low-alloy Cr-Mo-V steel after austenitization in the intercritical temperature range
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Structure and properties of low-alloy Cr-Mo-V steel after austenitization in the intercritical temperature range
Do you wish to request the book?
Structure and properties of low-alloy Cr-Mo-V steel after austenitization in the intercritical temperature range
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Structure and properties of low-alloy Cr-Mo-V steel after austenitization in the intercritical temperature range
2014
Overview
The structure formation in 26X1MΦA steel as a result of double quenching (the second time from the intercritical temperature range
A
c
1
-
A
c
2
) and high tempering is established. By EBSD, the crystallographic features of the ferritic-martensitic structure formed in single and double quenching and stabilized on tempering are studied. The prospects for improving the mechanical properties of low-alloy, low-carbon Cr-Mo-V steel by quenching from the intercritical temperature range are considered
Publisher
Allerton Press,Springer Nature B.V