Asset Details
Do you wish to reserve the book?
A Study on the Application Performance of High-Aspect-Ratio Nano-Ettringite in Photocurable Resin Composites
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
A Study on the Application Performance of High-Aspect-Ratio Nano-Ettringite in Photocurable Resin Composites
Do you wish to request the book?
A Study on the Application Performance of High-Aspect-Ratio Nano-Ettringite in Photocurable Resin Composites
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
A Study on the Application Performance of High-Aspect-Ratio Nano-Ettringite in Photocurable Resin Composites
2024
Overview
In this study, the impact of the addition of high-aspect-ratio nano-ettringite to photocurable epoxy acrylate resin was explored. The nano-ettringite samples were modified using γ-Aminopropyltriethoxysilane (KH-550) and γ-methacryloxypropyl trimethoxy silane (KH-570). Then, 3 wt% or 6 wt% KH-550-modified, KH-570-modified, and unmodified nano-ettringite samples were dispersed into resin via ultrasonic treatment in conjunction with mechanical stirring. The grafting effects of nano-ettringite onto KH-550 or KH-570 were analyzed through scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), and thermogravimetric (TG) analysis. The results demonstrate that KH-550 and KH-570 have been successfully grafted onto the surface of nano-ettringite. In addition, this study also focuses on the variations of composite materials in the viscosity, shrinkage, tensile strength, and elongation at break. The results indicate that increased dosages of unmodified, KH-550-modified, and KH-570-modified nano-ettringite led to increased viscosity of the composite while reducing shrinkage. At the same dosage, the photocurable resin containing KH-570-modified nano-ettringite demonstrated a lower shrinkage and a higher tensile strength. From the analysis of tensile fracture surfaces, it was observed that compared to the KH-550 modified and unmodified variants, the KH-570 modified nano-ettringite exhibits superior dispersibility in photocurable epoxy acrylate resin. Notably, when the amount of KH-570-modified nano-ettringite was 3 wt%, the highest tensile strength of the composite was 64.61 MPa, representing a 72.57% increase compared to the blank sample. Furthermore, the incorporation of KH-570-modified nano-ettringite as a filler provides a new perspective for improving the performance of photocurable epoxy acrylate resin composites.