Asset Details
Do you wish to reserve the book?
Effect of Tempering Time on Carbide Evolution and Mechanical Properties of a Nb-V-Ti Micro-Alloyed Steel
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of Tempering Time on Carbide Evolution and Mechanical Properties of a Nb-V-Ti Micro-Alloyed Steel
Do you wish to request the book?
Effect of Tempering Time on Carbide Evolution and Mechanical Properties of a Nb-V-Ti Micro-Alloyed Steel
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of Tempering Time on Carbide Evolution and Mechanical Properties of a Nb-V-Ti Micro-Alloyed Steel
2023
Overview
The evolution of the microstructure, the precipitation behavior, and the mechanical performances of Nb-V-Ti micro-alloyed steel prepared under different tempering time were studied using transmission electron microscopy (TEM), X-ray diffraction (XRD), and mechanical tests. It was found that the width of the martensite laths increases with the increasing tempering time. Several kinds of carbides, including M3C, M2C, M23C6, M7C3, and MC particles, were identified after tempering. The MC carbides remain stable during tempering, but the transformation behavior of other carbides was identified. The transformation sequence can be summarized as: M3C → M2C → M7C3 → M23C6. The strength decreases and the Charpy impact toughness increases gradually with the increase in the tempering time. The ultimate strength (UTS) decreases from 1231 to 896 MPa, and the yield strength (YS) decreases from 1138 to 835 MPa. The −40 °C Charpy impact toughness increases from 20 to 61 J as the tempering time increases from 10 min to 100 h. The evolution of carbides plays an important role in their mechanical performances.