Asset Details
Do you wish to reserve the book?
Deposition of Multilayer Nanostructured Coating Cr/(Cr/a-C)ml on Alloy Steels
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Deposition of Multilayer Nanostructured Coating Cr/(Cr/a-C)ml on Alloy Steels
Do you wish to request the book?
Deposition of Multilayer Nanostructured Coating Cr/(Cr/a-C)ml on Alloy Steels
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Deposition of Multilayer Nanostructured Coating Cr/(Cr/a-C)ml on Alloy Steels
2025
Overview
A chromium/amorphous carbon (Cr/(Cr/a-C)ml) nanostructured multilayer coating with a chromium sublayer was deposited on 42CrMo4 (1.7225,BDS EN ISO 683-2:2018), 100Cr6 (1.3505, BDS EN ISO 683-17:2024), and HS18-0-1 (1.3355, BDS EN ISO 4957:2018) alloy steels, selected for their use in contact-loaded components subjected to cyclic fatigue and intense wear. The coating was sputter deposited by MF pulsed magnetron sputtering under consistent process parameters. The resulting coating, approximately 1.8 μm thick, can significantly enhance the service life of these components. Adhesion was evaluated via the Daimler–Benz test, while coating homogeneity was confirmed through energy-dispersive spectroscopy, revealing a consistent chemical composition across sample surfaces. Raman spectroscopy indicated a high sp3/sp2 ratio, confirming a dominant diamond-like carbon structure. Nanoindentation measurements verified the coating’s hardness, aligning with the observed structural properties. These results validate the process parameters for depositing a Cr/(Cr/a-C)ml coating on these alloy steels, achieving this study’s objectives.