Asset Details
Do you wish to reserve the book?
Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag
Do you wish to request the book?
Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag
2015
Overview
Experimental studies on the rheological properties of a Ca O–Si O2–Al2O3–Mg O–Ti O2–(Ti C) blast furnace(BF) slag system were conducted using a high-temperature rheometer to reveal the non-Newtonian behavior of heterogeneous titanium-bearing molten slag. By measuring the relationships among the viscosity, the shear stress and the shear rate of molten slags with different Ti C contents at different temperatures, the rheological constitutive equations were established along with the rheological parameters; in addition, the non-Newtonian fluid types of the molten slags were determined. The results indicated that, with increasing Ti C content, the viscosity of the molten slag tended to increase. If the Ti C content was less than 2wt%, the molten slag exhibited the Newtonian fluid behavior when the temperature was higher than the critical viscosity temperature of the molten slag. In contrast, the molten slag exhibited the non-Newtonian pseudoplastic fluid characteristic and the shear thinning behavior when the temperature was less than the critical viscosity temperature. However, if the Ti C content exceeded 4wt%, the molten slag produced the yield stress and exhibited the Bingham and plastic pseudoplastic fluid behaviors when the temperature was higher and lower than the critical viscosity temperature, respectively. When the Ti C content increased further, the yield stress of the molten slag increased and the shear thinning phenomenon became more obvious.