Asset Details
Do you wish to reserve the book?
Luminescence properties of Ge and Ge-Si structures on silicon-based microcavities
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Luminescence properties of Ge and Ge-Si structures on silicon-based microcavities
Do you wish to request the book?
Luminescence properties of Ge and Ge-Si structures on silicon-based microcavities
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Luminescence properties of Ge and Ge-Si structures on silicon-based microcavities
2025
Overview
Utilizing laser etching technology under specific laser parameters (laser energy 250 mJ, repetition rate 1 Hz, pulse width 30 ns, spot diameter 150 µm), single-crystal silicon was etched, followed by the deposition of materials onto silicon-based microcavity samples using the pulsed laser deposition method. The Ge-coated microcavity samples were characterized using SEM and EDS, revealing cluster formations at the edges of the microcavities with the presence of germanium within these clusters. Photoluminescence spectroscopy identified characteristic luminescence peaks due to transverse optical (TO) phonon vibrations at 695 nm in the Ge-coated microcavity samples. Subsequently, the Ge-coated microcavity samples were subjected to high-temperature annealing at 1000 °C. After annealing for 30 min, a sharp luminescence peak at 700 nm associated with Ge-O bonds was observed. Finally, a layer of Si was deposited over the Ge-coated samples using pulsed laser deposition, resulting in a Ge-Si bilayer structure. After annealing at 1000 °C, this bilayer structure exhibited two distinctive peaks at 700 nm and 940 nm, with the former being a sharp peak due to Ge-O bonds and the latter due to the formation of Si-Si bonds within the clusters.