Asset Details
Do you wish to reserve the book?
Electroless Nickel Plating on AM60B Magnesium Alloy via Ti-Zr/Sol-Gel Composite Layer as Pretreatment
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Electroless Nickel Plating on AM60B Magnesium Alloy via Ti-Zr/Sol-Gel Composite Layer as Pretreatment
Do you wish to request the book?
Electroless Nickel Plating on AM60B Magnesium Alloy via Ti-Zr/Sol-Gel Composite Layer as Pretreatment
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Electroless Nickel Plating on AM60B Magnesium Alloy via Ti-Zr/Sol-Gel Composite Layer as Pretreatment
2022
Overview
The Ti-Zr and Ti-Zr/sol-gel were used as pretreatment layers before the electroless nickel coating on AM60B magnesium alloy. Scanning Electron Microscopy was employed to investigate the surface morphology of the pretreated layers and applied electroless coatings. Chemical analysis of the Ti-Zr layer, and nickel coatings was done using the Energy-Dispersive X-ray Spectroscopy. Moreover, the X-ray Diffraction and Atomic Force Microscopy methods were utilized to evaluate the microstructure and surface roughness of the electroless coatings, respectively. Electrochemical Impedance Spectroscopy was employed to study the corrosion behavior of Ni-P coatings. The results show that Ti-Zr layer has structural cracks, and the sol-gel film was covered all cracks entirely. The cauliflower-like electroless nickel coating was applied on both mentioned pretreated layers. The cross-sectional images revealed the higher thickness for the electroless coating on Ti-Zr/sol-gel layer, probably due to a large number of Ni nucleation centers. The EIS results demonstrate that the electroless coating on Ti-Zr/sol-gel has high corrosion protection and microhardness value.