Asset Details
Do you wish to reserve the book?
Manufacturing of Ti-Nb-Cr-V-Ni-Al Refractory High-Entropy Alloys Using Direct Energy Deposition
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Manufacturing of Ti-Nb-Cr-V-Ni-Al Refractory High-Entropy Alloys Using Direct Energy Deposition
Do you wish to request the book?
Manufacturing of Ti-Nb-Cr-V-Ni-Al Refractory High-Entropy Alloys Using Direct Energy Deposition
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Manufacturing of Ti-Nb-Cr-V-Ni-Al Refractory High-Entropy Alloys Using Direct Energy Deposition
2022
Overview
High-entropy alloys (HEAs) are composed of 5–35 at% of five or more elements, have high configurational entropy, do not form intermetallic compounds, and have a single-phase face-centered cubic structure or body-centered cubic structure. In particular, refractory HEAs (RHEAs), based on refractory materials with excellent mechanical properties at high temperatures, have high strength and hardness at room temperature and excellent mechanical properties at low and high temperatures. In this study, the Ti-Nb-Cr-V-Ni-Al RHEAs were deposited using direct energy deposition (DED). In the microstructure of Ti-Nb-Cr-V-Ni-Al, the sigma, BCC A2, and Ti2Ni phases appeared to be different from the BCC A2, BCC B2, and Laves phases predicted in the phase diagram. This microstructure was similar to that of the casted Ti-Nb-Cr-V-Ni-Al and had a constructed fine grain size. It was found that the growth of these microstructures was due to the DED process, which has a fast solidification rate. The fine grain size caused high hardness, and the microhardness of the Ti-Nb-Cr-V-Ni-Al was measured to be about 900 HV. In addition, in order to analyze the thermal properties of Ti-Nb-Cr-V-Ni-Al composed of the refractory material, the heat-affected zone (HAZ) was analyzed through a preheating test. The HAZ was decreased, owing to the high thermal diffusivity of Ti-Nb-Cr-V-Ni-Al.