Application of Micro-Arc Discharges during Anodization of Tantalum for Synthesis of Photocatalytic Active Ta2O5 Coatings
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Application of Micro-Arc Discharges during Anodization of Tantalum for Synthesis of Photocatalytic Active Ta2O5 Coatings
Do you wish to request the book?
Application of Micro-Arc Discharges during Anodization of Tantalum for Synthesis of Photocatalytic Active Ta2O5 Coatings
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Application of Micro-Arc Discharges during Anodization of Tantalum for Synthesis of Photocatalytic Active Ta2O5 Coatings
2023
Overview
Ta2O5 coatings were created using micro-arc discharges (MDs) during anodization on a tantalum substrate in a sodium phosphate electrolyte (10 g/L Na3PO4·10H2O). During the process, the size of MDs increases while the number of MDs decreases. The elements and their ionization states present in MDs were identified using optical emission spectroscopy. The hydrogen Balmer line Hβ shape analysis revealed the presence of two types of MDs, with estimated electron number densities of around 1.1 × 1021 m−3 and 7.3 × 1021 m−3. The effect of MDs duration on surface morphology, phase and chemical composition, optical absorption, and photoluminescent, properties of Ta2O5 coatings, as well as their applications in photocatalytic degradation of methyl orange, were investigated. The created coatings were crystalline and were primarily composed of Ta2O5 orthorhombic phase. Since Ta2O5 coatings feature strong absorption in the ultraviolet light region below 320 nm, their photocatalytic activity is very high and increases with the time of the MDs process. This was associated with an increase of oxygen vacancy defects in coatings formed during the MDs, which was confirmed by photoluminescent measurements. The photocatalytic activity after 8 h of irradiation was around 69%, 74%, 80%, and 88% for Ta2O5 coatings created after 3 min, 5 min, 10 min, and 15 min, respectively.