Asset Details
Do you wish to reserve the book?
Catalytic Preparation of Carbon Nanotubes from Waste Polyethylene Using FeNi Bimetallic Nanocatalyst
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Catalytic Preparation of Carbon Nanotubes from Waste Polyethylene Using FeNi Bimetallic Nanocatalyst
Do you wish to request the book?
Catalytic Preparation of Carbon Nanotubes from Waste Polyethylene Using FeNi Bimetallic Nanocatalyst
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Catalytic Preparation of Carbon Nanotubes from Waste Polyethylene Using FeNi Bimetallic Nanocatalyst
2020
Overview
In this work, carbon nanotubes (CNTs) were synthesized by catalytic pyrolysis from waste polyethylene in Ar using an in-situ catalyst derived from ferric nitrate and nickel nitrate precursors. The influence factors (such as temperature, catalyst content and Fe/Ni molar ratio) on the formation of CNTs were investigated. The results showed that with the temperature increasing from 773 to 1073 K, the carbon yield gradually increased whereas the aspect (length-diameter) ratio of CNTs initially increased and then decreased. The optimal growth temperature of CNTs was 973 K. With increasing the Fe/Ni molar ratio in an FeNi bimetallic catalyst, the yield of CNTs gradually increased, whereas their aspect ratio first increased and then decreased. The optimal usage of the catalyst precursor (Fe/Ni molar ratio was 5:5) was 0.50 wt% with respect to the mass of polyethylene. In this case, the yield of CNTs reached as high as 20 wt%, and their diameter and length were respectively 20–30 nm, and a few tens of micrometers. The simple low-cost method developed in this work could be used to address the environmental concerns about plastic waste, and synthesize high value-added CNTs for a range of future applications.